Product application

Application: It is suitable for coating as a primer on the surface of various steel facilities subject to corrosion by chemical and industrial atmospheres, and can also be used as a primer on the surface of concrete facilities.

Product color and composition

Colour: iron red, grey

Composition It is composed of high chlorinated polyethylene, epoxy resin, plasticizer, mica iron oxide, anti-settling agent, solvent, etc. As mica iron oxide is a flaky pigment, the pigment components can be arranged in a directional and parallel overlapping manner, forming a "fish scale" -like overlap. In the composition, it is combined with other anti-corrosion pigments, so the coating has excellent anti-rust properties, good weather resistance, tough film, strong adhesion, and fast drying. Good anti-corrosion performance.

Technical parameters

Coating methods: Brushing, roller coating or spraying

The surface drying time at 25℃ is no more than 2 hours

Practical work ≤24 hours

The coating interval temperature is 0℃, 20℃ and 30℃

The shortest time is 24 hours, 8 hours or 6 hours

Up to 7 days, 7 days, 7 days

The reference dosage is 2 to 3 square meters per kilogram

The wet film thickness is 130-160 microns, and the dry film thickness is 65-80 microns.

Diluent: High chlorination diluent, with a dosage of 10-15% (by weight, depending on specific circumstances)

Post-treatment coatings: high chlorinated polyethylene anti-corrosion intermediate paint, high chlorinated polyethylene anti-corrosion topcoat.

Shelf life: 12 months

Packaging specification: 20kg per drum