Product application

Application: It has excellent resistance to moisture, water, chemicals and chemical atmosphere, and good anti-rust performance. The bottom surface has good adhesion, strong bonding force and dries quickly. The one-time film thickness can reach 45-50 microns, which can reduce the number of construction passes and facilitate the construction process. It is suitable for anti-corrosion intermediate coatings on various structural surfaces that are subject to corrosion by chemical atmospheres, industrial atmospheres, and acids, alkalis, and salts. It can also be used as an intermediate coating for anti-corrosion coatings on the surfaces of concrete facilities.

Product color and composition

Color: Iron red, gray

Composition: It is composed of high chlorinated polyethylene, epoxy resin, plasticizer, flake anti-rust pigment, stabilizer, anti-settling agent, solvent, etc

Technical parameters

Coating methods: Brushing, roller coating or spraying

The surface drying time at 25℃ is no more than 2 hours

Practical work ≤24 hours

The coating interval temperature is 0℃, 20℃ and 30℃

The shortest time is 24 hours, 8 hours or 6 hours

Up to 7 days, 7 days, 7 days

Reference dosage: 1-2m ² /kg

The wet film thickness is 170 to 190 microns, and the dry film thickness is 85 to 95 microns.

Diluent: High chlorination diluent, with a dosage of 10-15% (by weight, depending on specific circumstances)

Pre-treatment coating: High chlorinated polyethylene mica iron anti-rust paint, high chlorinated polyethylene anti-rust paint.

Post-treatment coating: high chlorinated polyethylene anti-corrosion topcoat.

Shelf life: 12 months

Packaging specification: 20kg per drum